Stainless Steel 410 is a materialistic stainless steel which is attractive, opposes consumption in mellow situations and has genuinely great flexibility. Stainless Steel 410 is utilized where scraped area and wear resistance is required, joined with reasonable imperviousness to general consumption and oxidation.
SPECIFICATIONS:
- ASTM/ASME: UNS S41000
- EURONORM: FeMi35Cr20Cu4Mo2
- DIN: 2.4660
FEATURES OF STAINLESS STEEL 410
- Martensitic stainless steel with high mechanical properties.
- Ferromagnetic in the strengthened or solidified condition.
- Contains least measure of chromium to grant stainless steel properties.
- Opposes oxidation and scaling up to 1200°F.
- Opposes scraped spot and wear well than most 300 arrangement stainless steels.
APPLICATIONS OF STAINLESS STEEL 410:
Applications obliging moderate erosion resistance and high mechanical properties are perfect for Alloy 410. Illustrations of uses that regularly utilized Alloy 410 include:
- Cutlery
- Steam and gas turbine sharpened pieces of steels
- Kitchen utensils
- Screws, nuts, screws
- Pump and valve parts and shafts
- Mine stepping stool floor coverings
- Dental and surgical instruments
- Spouts
- Solidified steel balls and seats for oil well pumps
TYPES OF STAINLESS STEEL 410:
- ASTM A312 TP 410 Stainless Steel Seamless Pipes
- SS 410 Welded Pipes
- ASTM A213 TP 410 Stainless Steel Seamless Tubes
- SS 410 Rectangular Pipes
- ASTM A312 TP 410 Stainless Steel Welded Pipes
- SS 410 Seamless Tubes
- ASTM A249 TP 410 Stainless Steel Welded Tubes
- SS 410 ERW Tubes
- SS 410 Seamless Pipes
- SS 410 EFW Tubes
- SS 410 ERW Pipes
- SS 410 Welded Tubes
- SS 410 EFW Pipes
- SS 410 Rectangular Tubes
- Stainless Steel 410 Round Bar
- Stainless Steel 410 plates
- Stainless Steel 410 sheets
- Stainless Steel 410 coil
- Stainless Steel 410 fitting
- Stainless Steel 410 flanges
- Stainless Steel 410 fasteners
CHEMICAL COMPOSITION OF STAINLESS STEEL 410:
| C | Mn | Si | P | S | Cr | Ni | |
|---|---|---|---|---|---|---|---|
| 410 | 0.15 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 max: 13.5 |
0.50 max |
MECHANICAL PROPERTIES OF STAINLESS STEEL 410:
| Grade | Tensile Strength ksi (MPa) min | Yield Strength 0.2% offset ksi (MPa) min | Elongation (% in 50mm) min | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
|---|---|---|---|---|---|
| 410 | 65 (450) | 30 (205) | 20 | 217 | 96 |
MECHANICAL PROPERTIES OF HEAT TREATED 410:
| Heat Treatment | T410 (0.14%C) Hardened 1800°F (982°C) | ||
|---|---|---|---|
| Rockwell Hardness | 0.2% YS, Ksi (MPa) | UTS, Ksi (MPa) | |
| Annealed* | 81 HRB | 45.4 (313) | 80.4 (554) |
| Hardened & Tempered 400°F (204°C) | 43 HRC | 156.1 (1076) | 202.9 (1399) |
| Hardened & Tempered 550°F (288°C) | 40 HRC | 148.3 (1022) | 187.0 (1289) |
| Hardened & Tempered 600°F (316°C) | 40 HRC | 148.8 (1026) | 186.1 (1283) |
| Hardened & Tempered 800°F (427°C) | 41 HRC | 132.9 (916) | 188.5 (1300) |
| Hardened & Tempered 900°F (482°C) | 41 HRC | 122.6 (845) | 154.3 (1063) |
| Hardened & Tempered 1000°F (538°C) | 35 HRC | 127.9 (882) | 154.3 (1063) |
| Hardened & Tempered 1200°F (649°C) | 98 HRB | 85.5 (589) | 111.2 (767) |
PHYSICAL PROPERTIES OF STAINLESS STEEL 410:
| Density lbm/in3 |
Thermal Conductivity (BTU/h ft. °F) |
Electrical Resistivity (in x 10-6) |
Modulus of Elasticity (psi x 106 |
Coefficient of Thermal Expansion (in/in)/ °F x 10-6 |
Specific Heat (BTU/lb/ °F) |
Melting Range (°F) |
|---|---|---|---|---|---|---|
| at 68°F: 0.276 | 14.4 at 212°F | 56 at 68°F | 29 | 5.90 at 68 – 392°F | 0.11 at 68°F to 212°F | 2700 to 2790 |
| 6.5 at 68 – 1112°F |